ASTM A395 / A395M – 99(2009) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
ASTM A395 / A395M
Abstract ASTM a395 pdf
This specification covers standard requirements for ductile iron castings for pressure-retaining parts for use at elevated temperatures. Castings are classified by grades based on mechanical property requirements. These iron castings shall meet the specified values of tensile strength, yield strength, elongation and hardness. Chemical analysis shall be performed wherein the casting shall conform to the required chemical composition for carbon, silicon, and phosphorous. The material shall meet the required tensile properties, hardness, and microstructure. The iron casting shall undergo pressure test after machining. The thickness of any repaired section in relation to the size of the plug used shall be indicated. The minimum radius of repaired sections of cylinders or cones in relation to the size of plug used shall not exceed the prescribed limit. Other defective areas may also be repaired by plugging provided the minimum ligament between plugs in adjacent areas shall not be less than twice the distance from the nearest plug. Three Y-blocks shall be utilized as test coupons. The material shall undergo the following test methods: tension test, chemical analysis, yield strength test, and hardness test.

 

This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

1. Scope

1.1 This specification covers ductile iron castings for pressure-retaining parts for use at elevated temperatures. Castings of all grades are suitable for use up to 450°F. For temperatures above 450°F and up to 650°F, only Grade 60–40–18 castings are suitable (Note 1).

1.2 Valves, flanges, pipe fittings, pumps, and other piping components are generally manufactured in advance and supplied from stock by the manufacturer, jobber, or dealer.

1.3 For supplemental casting requirements, Specification A 834 may be utilized.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

Note 1—For service other than as specified in this section, reference should be made to Specification A 536 for Ductile Iron Castings.

2. Referenced Documents (purchase separately)

ASTM Standards

A247 Test Method for Evaluating the Microstructure of Graphite in Iron Castings
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A536 Specification for Ductile Iron Castings
A732/A732M Specification for Castings, Investment, Carbon and Low Alloy Steel for General Application, and Cobalt Alloy for High Strength at Elevated Temperatures
A834 Specification for Common Requirements for Iron Castings for General Industrial Use
E8 Test Methods for Tension Testing of Metallic Materials
E10 Test Method for Brinell Hardness of Metallic Materials
E186 Reference Radiographs for Heavy-Walled (2 to 412-in. [51 to 114-mm]) Steel Castings
E280 Reference Radiographs for Heavy-Walled (412 to 12-in. [114 to 305-mm]) Steel Castings
E446 Reference Radiographs for Steel Castings Up to 2 in. [51 mm] in Thickness
E689 Reference Radiographs for Ductile Iron Castings
E1806 Practice for Sampling Steel and Iron for Determination of Chemical Composition
F1476 Specification for Performance of Gasketed Mechanical Couplings for Use in Piping Applications
F1548 Specification for Performance of Fittings for Use with Gasketed Mechanical Couplings Used in Piping Applications
Manufacturers Standardization Society of the Valve and Fittings Industry Standard

SP25 Standard Marking Systems for Valves, Flanges, Pipe Fittings, and Unions

Index Terms

casting; ductile iron; mechanical properties; pressure-retaining; pressure test; tensile strength; tension testing; yield strength; Ductile iron castings–specifications; Elevated temperature service applications–steel; Pressure pipelines/piping systems–specifications; Pressure-retaining parts; Pressure vessel iron;

File Type Download : PDF File, ASTM a395



astm a247 latest free download, astm a395, ASTM a395 vs A536, ASTM a395 Chemical Composition, ASTM A-395, a536 vs a395 ductile iron, A536 A395, a395 chemical composition, ASTM A-536 and ASTM A-395, free copy of ASTM B367 pdf